Thin Wall Tubing

NON FLAME RETARDANT POLYOLEFIN TUBING SHRINK RATIO 2:1 BH-1

info@flypower-heatshrink.com (Super User) — Tue, 10 Dec 2013 18:16:25 +0800

BH-1 NON FLAME RETARDANT POLYOLEFIN TUBING SHRINK RATIO 2:1

{tab=Specification}

Normal Size(mm)	As supplied(mm)		After recovered (mm)		Standard length (m/spool)
Normal Size(mm)	Inside diameter (mm)	Wall thickness (mm)	Inside diameter (max)	Wall thickness (min)	Standard length (m/spool)
Φ1.0	1.5±0.2	0.18	0.5	0.33	200
Φ1.5	2.0±0.2	0.18	0.75	0.33	200
Φ2.0	2.7±0.2	0.25	1	0.44	200
Φ2.5	3.1±0.2	0.25	1.25	0.44	200
Φ3.0	3.7±0.3	0.25	1.5	0.44	200
Φ3.5	4.0±0.3	0.25	1.75	0.44	200
Φ4.0	4.7±0.3	0.25	2	0.44	200
Φ5.0	5.6±0.3	0.25	2.5	0.5	100
Φ6.0	6.8±0.3	0.25	3	0.5	100
Φ7.0	7.7±0.3	0.25	3.5 0	0.56	100
Φ8.0	8.8±0.3	0.3	4	0.56	100
Φ9.0	9.8±0.3	0.3	4.5	0.56	100
Φ10	10.7±0.4	0.3	5	0.56	100
Φ11	11.7±0.4	0.3	5. 50	0.56	100
Φ12	12.7±0.4	0.3	6	0.56	50
Φ13	13.7±0.4	0.35	6.5	0.69	50
Φ14	14.7±0.4	0.35	7	0.69	50
Φ15	15.7±0.5	0.35	7.5	0.69	50
Φ16	16.7±0.5	0.35	8	0.69	50
Φ18	19.0±0.5	0.4	9	0.77	50
Φ20	21.4±0.5	0.4	10	0.89	50
Φ22	23.4±0.6	0.45	11	0.89	50
Φ25	26.5±0.8	0.45	12	0.89	50
Φ28	29.5±0.8	0.45	14	0.95	50
Φ30	31.5±0.8	0.45	15	0.95	50
Φ35	36.5±0.8	0.5	17.5	1.1	50
Φ40	42.0±0.8	0.5	20	1.1	50
Φ50	52.0±0.8	0.5	25	1.15	50

Special size, cut pieces are available on request.

{tab=Technical Data}

Property	Test Method	Typical Data
Operating temperature	UL 224	-55 to +105℃
Tensile strength	ASTM D 2671	>10.4MPa
Elongation at break	ASTM D 2671	>500%
Longitudinal shrinkage	UL 224	+/- 5%
Eccentricity	ASTM D 2671	<30%
Flammability	-----	Flammable
Dielectric strength	IEC93	>25KV/mm
Volume resistance	ASTM D 2671	>1014 Ω.cm
Copper stability	ISO62	Pass

{/tabs}

3:1 SHRINK RATIO FLEXIBLE THIN WALL FLAME RETARDANT POLYOLEFIN TUBING BH-2

info@flypower-heatshrink.com (Super User) — Mon, 14 Apr 2014 10:28:46 +0800

BH-2 3:1 SHRINK RATIO FLEXIBLE THIN WALL FLAME RETARDANT POLYOLEFIN TUBING

{tab=Specification}

Normal size		As supplied (mm)		After recovered (mm)		Standard length (m/spool)
mm	Inch	Inside diameter	Wall thickness（mm）	Inside diameter	Wall thickness（mm）	Standard length (m/spool)
1.5/0.5	1/16	1.6	0.15	0.5	0.45	200
3.0/1.0	1/8	3.2	0.18	1.0	0.55	200
4.5/1.5	3/16	4.8	0.20	1.5	0.60	100
6.0/2.0	1/4	6.4	0.22	2.0	0.65	100
9.0/3.0	3/8	9.5	0.25	3.0	0.75	100
12.0/4.0	1/2	12.7	0.25	4.0	0.80	50
18.0/6.0	3/4	19.1	0.35	6.0	0.90	50
24.0/8.0	1	25.4	0.45	8.0	1.00	50
39.0/13.0	1 1/2	39.0	0.50	13.0	1.25	50

Special size, cut pieces are available on request.

{tab=Technical Data}

Property	Test Method	Typical Data
Operating temperature	UL 224	-55 to +125℃
Tensile strength	ASTM D 2671	>14MPa
Elongation at break	ASTM D 2671	>400%
Longitudinal shrinkage	UL 224	0--10%
Eccentricity	ASTM D 2671	<30%
Elongation at break after aging	158℃, 168 hrs.	>300%
Flammability	VW-1	Pass
Dielectric strength	IEC243	>20KV/mm
Volume resistance	IEC93	>10¹⁴Ω.cm
Copper stability	ASTM D 2671	Pass

{/tabs}

ULTRA THIN WALL FLEXIBLE ENVIRONMENT FRIENDLY FLAME RETARDANT POLYOLEFIN HEAT SHRINK TUBING SHRINK RATIO 2:1 BH-2(CB)

info@flypower-heatshrink.com (Super User) — Tue, 15 Apr 2014 10:55:28 +0800

ULTRA THIN WALL FLEXIBLE ENVIRONMENT FRIENDLY FLAME RETARDANT POLYOLEFIN HEAT SHRINK TUBING SHRINK RATIO 2:1 BH-2(CB)

{tab=Specification}

Size （mm）	As supplied（mm）		After recovered（mm）		Packing	Application Cable
Size （mm）	ID	Thickness	ID	Thickness	Meters/Spool	（mm)
Φ 0.6CB	0.90±0.2	0.13±0.05	≤0.40	0.20±0.10	200	0.40～0.70
Φ 0.8CB	1.10±0.2	0.13±0.05	≤0.50	0.20±0.10	200	0.60～0.80
Φ 1.0CB	1.40±0.2	0.13±0.05	≤0.65	0.20±0.10	200	0.75～0.95
Φ 1.5CB	1.90±0.2	0.13±0.05	≤0.85	0.20±0.10	200	0.95～1.35
Φ 2.0CB	2.40±0.2	0.13±0.05	≤1.00	0.22±0.10	200	1.10～1.75
Φ 2.5CB	2.90±0.2	0.13±0.05	≤1.30	0.25±0.10	200	1.45～2.15
Φ 3.0CB	3.40±0.2	0.13±0.05	≤1.50	0.28±0.10	200	1.65～2.55
Φ 3.5CB	3.90±0.2	0.13±0.05	≤1.80	0.28±0.10	200	2.00～2.95
Φ 4.0CB	4.40±0.2	0.15±0.05	≤2.00	0.30±0.10	200	2.20～3.35
Φ 4.5CB	4.90±0.2	0.15±0.05	≤2.30	0.30±0.10	100	2.55～3.75
Φ 5.0CB	5.50±0.2	0.15±0.05	≤2.5	0.32±0.10	100	2.75～4.20
Φ 6.0CB	6.50±0.2	0.15±0.05	≤3.0	0.32±0.10	100	3.30～5.00
Φ 7CB	7.50±0.3	0.15±0.05	≤3.5	0.32±0.10	200	3.85～5.70
Φ 8CB	8.50±0.3	0.15±0.05	≤4.0	0.32±0.10	200	4.40～6.50
Φ 9CB	9.50±0.3	0.15±0.05	≤4.5	0.35±0.10	200	5.00～7.30
Φ 10CB	10.5±0.3	0.15±0.05	≤5.0	0.35±0.10	200	5.50～8.10
Φ 11CB	11.5±0.3	0.18±0.05	≤5.5	0.40±0.10	200	6.10～8.90
Φ 12CB	12.5±0.3	0.20±0.05	≤6.0	0.40±0.10	200	6.60～9.70
Φ 13CB	13.5±0.3	0.20±0.05	≤6.5	0.40±0.10	200	7.20～10.5
Φ 14CB	14.5±0.3	0.20±0.05	≤7.0	0.40±0.10	200	7.70～11.3
Φ 15CB	15.5±0.4	0.20±0.05	≤7.5	0.40±0.10	200	8.30～12.0
Φ 16CB	16.5±0.4	0.22±0.05	≤8.0	0.40±0.10	200	8.80～12.8
Φ 17CB	17.5±0.4	0.22±0.05	≤8.5	0.40±0.10	200	9.40～13.6
Φ 18CB	18.5±0.4	0.22±0.05	≤9.0	0.42±0.10	200	9.90～14.4
Φ 20CB	20.5±0.5	0.25±0.05	≤10.0	0.45±0.10	200	11.0～16.0
Φ 22CB	22.5±0.5	0.25±0.05	≤11.0	0.45±0.10	200	12.1～17.6
Φ 25CB	25.5±0.5	0.25±0.05	≤12.5	0.45±0.10	100	13.8～20.0

Special size, cut pieces are available on request.

{tab=Technical Data}

Property	Test Method	Typical Data
Operating temperature	IEC 216	-55 to +125℃
Tensile strength	ASTM D 2671	>14MPa
Elongation at break	ASTM D 2671	>400%
Longitudinal shrinkage	UL 224	0 to -5%
Eccentricity	ASTM D 2671	<30%
Elongation at break after aging	158℃/168 hrs.	>300%
Flammability	VW-1	Pass
Dielectric strength	IEC243	>20KV/mm
Volume resistance	IEC93	>10¹⁴Ω.cm
Copper stability	UL 224	Pass

{/tabs}

LOW SMOKING HALOGEN FREE FLAME RETARDANT HEAT SHRINKABLE TUBING SHRINK RATIO 2:1 BH-2(HF)

info@flypower-heatshrink.com (Super User) — Tue, 15 Apr 2014 14:53:38 +0800

LOW SMOKING HALOGEN FREE FLAME RETARDANT HEAT SHRINKABLE TUBING 2:1 BH-2(HF)

{tab=Specification}

Normal Size(mm)	As supplied(mm)		After recovered (mm)		Standard length(m/spool)
Normal Size(mm)	Inside diameter(mm)	Wall thickness(mm)	Inside diameter(Max.)	Wall thickness(mm)	Standard length(m/spool)
Φ1.0	1.5±0.2	0.18	0.50	0.33	200
Φ1.5	2.0±0.2	0.18	0.75	0.36	200
Φ2.0	2.7±0.2	0.25	1.00	0.44	200
Φ2.5	3.1±0.2	0.25	1.25	0.44	200
Φ3.0	3.7±0.3	0.25	1.50	0.44	200
Φ3.5	4.0±0.3	0.25	1.75	0.44	200
Φ4.0	4.7±0.3	0.25	2.00	0.44	200
Φ5.0	5.6±0.3	0.25	2.50	0.56	100
Φ6.0	6.8±0.3	0.25	3.00	0.56	100
Φ7.0	7.7±0.3	0.25	3.50	0.56	100
Φ8.0	8.8±0.3	0.30	4.00	0.56	100
Φ9.0	9.8±0.3	0.30	4.50	0.56	100
Φ10	10.7±0.4	0.30	5.00	0.56	100
Φ11	11.7±0.4	0.30	5.50	0.56	100
Φ12	12.7±0.4	0.30	6.00	0.56	50
Φ13	13.7±0.4	0.30	6.50	0.65	50
Φ14	14.7±0.4	0.35	7.00	0.69	50
Φ15	15.7±0.5	0.35	7.50	0.69	50
Φ16	16.7±0.5	0.35	8.00	0.69	50
Φ18	19.0±0.5	0.40	9.00	0.80	50
Φ20	21.4±0.5	0.40	10.00	0.80	50
Φ22	23.4±0.6	0.45	11.00	0.80	50
Φ25	26.5±0.8	0.45	12.50	0.90	50
Φ28	29.5±0.8	0.45	14.00	0.90	50
Φ30	31.5±0.8	0.45	15.00	0.90	50
Φ35	36.5±0.8	0.50	17.50	0.90	50
Φ40	42.0±0.8	0.50	20.00	1.00	50
Φ50	52.0±0.8	0.50	25.00	1.00	50
Φ60	62.0±1.0	0.50	30.00	1.00	30
Φ70	72.0±1.0	0.50	35.00	1.20	30
Φ80	82.0±1.0	0.55	40.00	1.20	30
Φ100	102.0±1.0	0.55	50.00	1.30	30
Φ125	126.0±1.0	0.55	60.00	1.30	15
Φ150	152.0±1.0	0.55	75.00	1.30	15

Special size, cut pieces are available on request.

{tab=Technical Data}

Property	Test Method	Typical Data
Operating temperature	IEC 216	-55 to +105℃
Tensile strength	ASTM D 2671	>10.4MPa
Elongation at break	ASTM D 2671	200%
Longitudinal shrinkage	UL224	±3%
Eccentricity	ASTM D 2671	≤30%
Heat shock	250℃/4hrs	No crack No dropping
Heat aging Tensile strength Ultimate elongation	136℃/168hrs	9.0MPa >150%
Flammability	SAE-AMS-DTL-23053/5	Pass

{/tabs}

ULTRA LOW TEMPERATURE FLEXIBLE HALOGEN FREE POLYOLEFIN TUBING SHRINK RATIO 2:1 BH-2(LS)

info@flypower-heatshrink.com (Super User) — Tue, 15 Apr 2014 16:29:44 +0800

ULTRA LOW TEMPERATURE FLEXIBLE HALOGEN FREE POLYOLEFIN TUBING SHRINK RATIO 2:1 BH-2(LS)

{tab=Specification}

Normal size	As supplied (mm)	After recovered (mm)		Standard length (m/spool)
(inch)	Inside diameter(mm)	Inside diameter(Max.)	Wall thickness(mm)	Standard length (m/spool)
1/16	1.6	0.8	0.50	200
3/64	2.4	1.2	0.50	200
1/8	3.2	1.6	0.50	200
3/16	4.8	2.4	0.50	200
1/4	6.4	3.2	0.60	100
5/16	8.0	4.0	0.60	100
3/8	9.5	4.8	0.60	100
1/2	12.7	6.4	0.60	50
5/8	16.0	8.0	0.60	50
3/4	19.1	9.5	0.80	50
1	25.4	12.7	0.90	50
1 1/4	31.8	15.9	0.90	50
1 1/2	38.1	19.1	1.00	50
2	50.8	25.4	1.10	50

Special size, cut pieces are available on request.

{tab=Technical Data}

Property	Test Method	Typical Data
Tensile strength	ASTM D 2671	13MPa
Elongation at break	ASTM D 2671	450%
Tensile strength after aging at 158℃for 168 hrs	ASTM D 2671	11MPa
Elongation after aging at 158℃for 168 hrs.	ASTM D 2671	300%
Heat shock (250℃/ 4 hrs.)	ASTM D 2671	No cracking
Cold bend test (-55℃/ 4 hrs.)	ASTM D 2671	No cracking
Copper Corrosion	UL 224	Pass
Flammability	MVSS 302	Pass
Fluid resistance	23℃for 24hrs ISO 37 tensile strength Elongation	11MPa 200%
Longitudinal shrinkage	UL 224	0±5%

{/tabs}

ENVIRONMENT FRIENDLY FLEXIBLE FLAME RETARDANT HEAT SHRINKABLE TUBING SHRINK RATIO 2:1 BH-2(Z)

info@flypower-heatshrink.com (Super User) — Tue, 15 Apr 2014 17:44:09 +0800

ENVIRONMENT FRIENDLY FLEXIBLE FLAME RETARDANT HEAT SHRINKABLE TUBING SHRINK RATIO 2:1 BH-2(Z)

{tab=Specification}

Normal Size(mm)	As supplied(mm)		After recovered (mm)		Standard length(m/spool)
Normal Size(mm)	Inside diameter(mm)	Wall thickness(mm)	Inside diameter (max)	Wall thickness(min)	Standard length(m/spool)
Φ1.0	1.5±0.2	0.18	0.50	0.33	200
Φ1.5	2.0±0.2	0.18	0.75	0.36	200
Φ2.0	2.7±0.2	0.25	1.00	0.44	200
Φ2.5	3.1±0.2	0.25	1.25	0.44	200
Φ3.0	3.7±0.3	0.25	1.50	0.44	200
Φ3.5	4.0±0.3	0.25	1.75	0.44	200
Φ4.0	4.7±0.3	0.25	2.00	0.44	200
Φ5.0	5.6±0.3	0.25	2.50	0.56	100
Φ6.0	6.8±0.3	0.25	3.00	0.56	100
Φ7.0	7.7±0.3	0.25	3.50	0.56	100
Φ8.0	8.8±0.3	0.30	4.00	0.56	100
Φ9.0	9.8±0.3	0.30	4.50	0.56	100
Φ10	10.7±0.4	0.30	5.00	0.56	100
Φ11	11.7±0.4	0.30	5.50	0.56	100
Φ12	12.7±0.4	0.30	6.00	0.56	50
Φ13	13.7±0.4	0.30	6.50	0.65	50
Φ14	14.7±0.4	0.35	7.00	0.69	50
Φ15	15.7±0.5	0.35	7.50	0.69	50
Φ16	16.7±0.5	0.35	8.00	0.69	50
Φ18	19.0±0.5	0.40	9.00	0.80	50
Φ20	21.4±0.5	0.40	10.00	0.80	50
Φ22	23.4±0.6	0.45	11.00	0.80	50
Φ25	26.5±0.8	0.45	12.50	0.90	50
Φ28	29.5±0.8	0.45	14.00	0.90	50
Φ30	31.5±0.8	0.45	15.00	0.90	50
Φ35	36.5±0.8	0.50	17.50	0.90	50
Φ40	42.0±0.8	0.50	20.00	1.00	50
Φ50	52.0±0.8	0.50	25.00	1.00	50
Φ60	62.0±1.0	0.50	30.00	1.00	30
Φ70	72.0±1.0	0.50	35.00	1.20	30
Φ80	82.0±1.0	0.55	40.00	1.20	30
Φ100	102.0±1.0	0.55	50.00	1.30	30
Φ125	126.0±1.0	0.55	60.00	1.30	15
Φ150	152.0±1.0	0.55	75.00	1.30	15

Special size, cut pieces are available on request.

{tab=Technical Data}

Property	Test Method	Typical Data
Operating temperature	UL 224	-55 to +125℃
Tensile strength	ASTM D 2671	>14MPa
Ultimate elongation	ASTM D 2671	400%
Longitudinal shrinkage	UL224	±5%
Eccentricity	ASTM D 2671	<30%
Heat aging Tensile strength Ultimate elongation	158℃/168hrs	12MPa >350%
Flammability	VW-1	Pass
Dielectric strength	IEC243	>20KV/mm
Volume resistance	IEC93	>10¹⁴Ω.cm
Copper stability	UL 224	Pass

{/tabs}

Medical grade peelable heat shrink tubing BH-2(PMT)

info@flypower-heatshrink.com (Super User) — Fri, 28 May 2021 09:43:42 +0800

Peelable heat shrink tubing BH-2(PMT)

{tab=Specification}

Model	Size (mm)	As Supplied (mm)	After Full Recovered(mm)
Model	Size (mm)	As Supplied (mm)	ID (D)	Wall Thickness(T)
BH-2(PMT)-0.8	0.80	1.02±0.13	0.33±0.05	0.25±0.05
BH-2(PMT)-1.2	1.20	1.35±0.13	0.40±0.08	0.45±0.08
BH-2(PMT)-1.6	1.60	1.83±0.13	0.69±0.10	0.51±0.08
BH-2(PMT)-2.4	2.40	2.72±0.20	1.07±0.10	0.51±0.08
BH-2(PMT)-3.2	3.20	3.56±0.25	1.45±0.13	0.51±0.08
BH-2(PMT)-4.8	4.80	5.21±0.25	2.18±0.18	0.51±0.08
BH-2(PMT)-6.4	6.40	6.99±0.38	2.97±0.20	0.51±0.08
BH-2(PMT)-9.5	9.50	10.54±0.51	4.34±0.41	0.64±0.08

Customized dimensions for your special application.

{/tabs}

Applications:

ENVIRONMENT FRIENDLY FLEXIBLE HIGHLY FLAME RETARDANT HEAT SHRINKABLE TUBING SHRINK RATIO 2:1 BH-2F

info@flypower-heatshrink.com (Super User) — Wed, 16 Apr 2014 08:50:37 +0800

ENVIRONMENT FRIENDLY FLEXIBLE HIGHLY FLAME RETARDANT HEAT SHRINKABLE TUBING SHRINK RATIO 2:1 BH-2F

{tab=Specification}

Normal Size(mm)	As supplied(mm)	After recovered (mm)		Standard length(m/spool)
Normal Size(mm)	Inside diameter(mm)	Inside diameter(Max.)	Wall thickness(Min.)	Standard length(m/spool)
3/64	1.2	0.60	0.40	200
1/16	1.6	0.80	0.40	200
3/32	2.4	1.20	0.48	200
1/8	3.2	1.60	0.48	200
3/16	4.8	2.40	0.48	100
1/4	6.4	3.20	0.56	100
5/16	8.0	4.00	0.62	100
3/8	9.5	4.80	0.62	50
1/2	12.7	6.40	0.62	50
5/8	15.9	8.00	0.68	50
3/4	19.1	9.50	0.68	50
1	25.4	12.70	0.87	50
11/4	31.8	15.90	1.00	50
11/2	38.1	19.10	1.00	50
2	50.8	25.40	1.10	50
3	76.2	38.10	1.20	30
4	102.0	50.80	1.35	30
5	125.0	63.50	1.40	15
6	151.0	75.00	1.40	15

Feet spool lengths are available subject to requirement;

Special size, cut pieces are available on request.

{tab=Technical Data}

Property	Test Method	Typical Data
Tensile strength	ASTM D 2671	14MPa
Elongation at break	ASTM D 2671	600%
Elongation after aging (175℃/ 168 hrs)	ASTM D 2671	350%
Flammability	UL 224 /VW-1 / SAE-AMS-DTL-23053/5	Pass
Heat shock (250 ℃/ 4hr hrs)	ASTM D 2671	No cracking
Cold bend test (-55℃/ 4 hrs)	ASTM D 2671	No cracking
Dielectric strength	ASTM D 150	20KV/mm
Volume resistance	ASTM D 876	1014Ω.cm
Copper Corrosion	UL 224	Pass
Water absorption	ASTM D 570	0.15%
Chemical resistance	SAE-AMS-DTL-23053/5	Pass
Longitudinal shrinkage	UL 224	0±5%
Eccentricity	UL 224	30%

{/tabs}

HIGHLY FLEXIBLE FLAME RETARDANT POLYOLEFIN HEAT SHRINK TUBING SHRINK RATIO 3:1 BH-2F(3X)

info@flypower-heatshrink.com (Super User) — Wed, 16 Apr 2014 15:13:45 +0800

HIGHLY FLEXIBLE FLAME RETARDANT POLYOLEFIN HEAT SHRINK TUBING SHRINK RATIO 3:1 BH-2F(3X)

{tab=Specification}

Normal size		As supplied (mm)		After recovered (mm)		Standard length (m/spool)
(mm)	(inch)	Inside diameter(Min.)	Wall thickness(mm)	Inside diameter(Max.)	Wall thickness(Min.)	Standard length (m/spool)
1.5/0.5	1/16	1.6	0.15	0.5	0.45	200
3.0/1.0	1/8	3.2	0.18	1.0	0.55	200
4.5/1.5	3/16	4.8	0.20	1.5	0.60	100
6.0/2.0	1/4	6.4	0.22	2.0	0.65	100
9.0/3.0	3/8	9.5	0.25	3.0	0.75	100
12.0/4.0	1/2	12.7	0.25	4.0	0.80	50
18.0/6.0	3/4	19.1	0.35	6.0	0.90	50
24.0/8.0	1	25.4	0.45	8.0	1.20	50
39.0/13.0	1 1/ 2	39.0	0.50	13.0	1.25	50

Special size, cut pieces are available on request.

{tab=Technical Data}

Property	Test Method	Typical Data
Tensile strength	ASTM D 2671	16MPa
Elongation at break	ASTM D 2671	800%
Tensile strength after aging at175℃for 168 hrs	ASTM D 2671	14MPa
Elongation after aging at175℃for 168 hrs.	ASTM D 2671	350%
Flammability	UL 224 / VW-1 SAE-AMS-DTL-23053/5	Pass
Heat shock (250℃/ 4 hrs.)	ASTM D 2671	No cracking
Cold bend test (-55℃/ 4 hrs.)	ASTM D 2671	No cracking
Dielectric strength	ASTM D 150	20KV/mm
Volume resistance	ASTM D 876	10¹⁴Ω .cm
Copper Corrosion	UL 224	Pass
Water absorption	ASTM D 570	0.15%
Chemical resistance	SAE-AMS-DTL-23053/5	Pass
Longitudinal shrinkage	UL 224	0±5%
Eccentricity	UL 224	30%

{/tabs}

HIGH FLEXIBLE FLAME RETARDANT POLYOLEFIN HEAT SHRINK TUBING SHRINK RATIO 4:1 BH-2F(4X)

info@flypower-heatshrink.com (Super User) — Wed, 16 Apr 2014 16:10:37 +0800

HIGH FLEXIBLE FLAME RETARDANT POLYOLEFIN HEAT SHRINK TUBING SHRINK RATIO 4:1 BH-2F(4X)

{tab=Specification}

Normal size		As supplied (mm)	After recovered (mm)		Standard length (m/spool)
(mm)	(inch)	Inside diameter(Min.)	Inside diameter(Max.)	Wall thickness(mm)	Standard length (m/spool)
19.1/4.6	3/4	19.1	4.6	1.7	1.22
25.4/7	1	25.4	7.0	1.7	1.22
38.1/9.5	11/2	38.1	9.5	1.7	1.22
50.8/14.0	2	50.8	14.0	1.7	1.22
76.2/20.6	3	76.2	20.6	1.7	1.22
102/26.7	4	102	26.7	1.7	1.22
115/36.8	41/2	115	36.8	1.7	1.22

Special size, cut pieces are available on request.

{tab=Technical Data}

Property	Test Method	Typical Data
Tensile strength	ASTM D 2671	16MPa
Elongation at break	ASTM D 2671	800%
Tensile strength after aging at 175℃for 168 hrs	ASTM D 2671	14MPa
Elongation after aging at175℃for 168 hrs.	ASTM D 2671	350%
Flammability	UL 224 /VW-1 SAE-AMS-DTL-23053/5	Pass
Heat shock (250℃/ 4 hrs.)	ASTM D 2671	No cracking
Cold bend test (-55℃/ 4 hrs.)	ASTM D 2671	No cracking
Dielectric strength	ASTM D 150	22KV/mm
Volume resistance	ASTM D 876	10¹⁴Ω .cm
Copper Corrosion	UL 224	Pass
Water absorption	ASTM D 570	0.15%
Chemical resistance	SAE-AMS-DTL-23053/5	Pass
Longitudinal shrinkage	UL 224	0±5%
Eccentricity	UL 224	30%

{/tabs}