High Temperature Tubing

150℃ HEAT SHRINKABLE FLEXIBLE THIN WALL PVDF(POLYVINYLIDENE FLUORIDE) TUBING BH-150K

info@flypower-heatshrink.com (Super User) — Wed, 23 Apr 2014 09:50:31 +0800

HEAT SHRINKABLE FLEXIBLE THIN WALL PVDF(POLYVINYLIDENE FLUORIDE) 150℃ TUBING BH-150K

{tab=Specification}

Normal size		As supplied (mm)	After recovered (mm)		Standard length (m/spool)
Inch	mm	Inside diameter (Min.)	Inside diameter (Max.)	Wall thickness（mm）	Standard length (m/spool)
3/64	1.2	1.2	0.60	0.25±0.05	200
1/16	1.6	1.6	0.80	0.25±0.05	200
3/32	2.4	2.4	1.20	0.25±0.04	200
1/8	3.2	3.2	1.60	0.25±0.04	200
3/16	4.8	4.8	2.40	0.25±0.04	100
1/4	6.4	6.4	3.20	0.30±0.05	100
3/8	9.5	9.5	4.80	0.30±0.05	100
1/2	12.7	12.7	6.40	0.30±0.05	100
3/4	19.1	19.1	9.50	0.43±0.07	50
1	25.4	25.4	12.70	0.48±0.07	50
1-1/4	31.8	31.8	15.9	0.51±0.08	50
1-1/2	38.1	38.1	19	0.51±0.07	50

{tab=Technical Data}

Property	Test Method	Typical Data
Operating temperature	IEC 216	-55 to +150℃
Tensile strength	ASTM D 2671	≥30MPa
Elongation at break	ASTM D 2671	≥150%
Elongation at break after aging	180℃, 168 hrs.	≥100%
Heat shock	250℃, 4 hrs.	No cracking
Cold bend	-55℃, 4 hrs.	No cracking
Flammability	VW-1	Pass
Volume resistance	IEC93	≥1013Ω.cm
Copper corrosion	180℃, 168 hrs.	No corrosion
Copper stability	180℃, 168 hrs.	No sign of degradation

{/tabs}

175℃ SEMI-RIGID PVDF (POLYVINYLIDENE FLUORIDE) HEAT SHRINKABLE TUBING BH-175K

info@flypower-heatshrink.com (Super User) — Sat, 26 Apr 2014 10:26:54 +0800

SEMI-RIGID PVDF (POLYVINYLIDENE FLUORIDE) HIGH TEMPERATURE CHEMICAL RESISTANT HEAT SHRINKABLE TUBING 175℃ BH-175K

{tab=Specification}

Normal size		As supplied (mm)	After recovered (mm)		Standard length (m/spool)
Inch	mm	Inside diameter (Min.)	Inside diameter (Max.)	Wall thickness（Nom.）	Standard length (m/spool)
3/64	1.2	1.2	0.6	0.25±0.05	200
1/16	1.6	1.6	0.8	0.25±0.05	200
3/32	2.4	2.4	1.2	0.25±0.05	200
1/8	3.2	3.2	1.6	0.25±0.05	200
3/16	4.8	4.8	2.4	0.25±0.05	100
1/4	6.4	6.4	3.2	0.30±0.08	100
3/8	9.5	9.5	4.8	0.30±0.08	100
1/2	12.7	12.7	6.4	0.30±0.08	100
3/4	19.1	19.1	9.5	0.43±0.08	50
1	25.4	25.4	12.70	0.48±0.08	50
1-1/4	31.8	31.8	15.9	0.51±0.08	50
1-1/2	38.1	38.1	19.1	0.51±0.08	50

Special size, cut pieces are available on request.

{tab=Technical Data}

Property	Test Method	Typical Data
Operating temperature	IEC 216	-55℃to +175℃
Tensile strength	ASTM D 2671	≥34.5 MPa
Elongation at break	ASTM D 2671	≥150%
Elongation at break after aging	250℃, 168 hrs.	≥100%
Heat shock	300℃, 1 hr	No cracking
Cold bend	-55℃, 1 hr.	No cracking
Flammability	VW-1	Pass
Volume resistance	IEC93	≥>10¹³Ω.cm
Dielectric strength	ASTM D 2671	≥30KV/mm

{/tabs}

200℃ Silicon rubber heat shrink tubing BH-SR200

info@flypower-heatshrink.com (Super User) — Wed, 29 Jun 2022 10:05:19 +0800

Silicon rubber heat shrink tubing BH-SR200

{tab=Specification}

Size	As supplied(mm)			Fully Recovered(mm)			Standard Package
Size	ID	Thin Type	Thick Type	ID	Thin Type	Thick Type	Meter/Spool or Meter/Pc
φ1.0	1.0	0.5±0.1	0.80±0.1	0.6	0.7±0.1	1.1±0.1	200
φ1.5	1.5	0.5±0.1	0.80±0.1	0.8	0.7±0.1	1.1±0.1	200
φ2.0	2.0	0.5±0.1	0.80±0.1	1.2	0.7±0.1	1.1±0.1	200
φ2.5	2.5	0.5±0.1	0.80±0.1	1.5	0.7±0.1	1.1±0.1	200
φ3.0	3.0	0.5±0.1	0.80±0.1	1.8	0.7±0.1	1.1±0.1	200
φ3.5	3.5	0.5±0.1	0.80±0.1	2.0	0.7±0.1	1.1±0.1	100
φ4.0	4.0	0.5±0.1	0.80±0.1	2.5	0.7±0.1	1.1±0.1	100
φ4.5	4.5	0.5±0.1	0.80±0.1	2.8	0.7±0.1	1.1±0.1	100
φ5.0	5.0	0.5±0.1	0.80±0.1	3.0	0.7±0.1	1.1±0.1	100
φ6.0	6.0	0.5±0.1	0.80±0.1	3.8	0.7±0.1	1.1±0.1	100
φ7.0	7.0	0.5±0.1	0.80±0.1	4.0	0.7±0.1	1.1±0.1	100
φ8.0	8.0	0.5±0.1	0.80±0.1	4.8	0.7±0.1	1.1±0.1	100
φ9.0	9.0	0.5±0.1	0.80±0.1	5.0	0.7±0.1	1.1±0.1	100
φ10.0	10.0	1.0±0.1	1.50±0.1	6.5	1.7±0.1	2.5±0.1	100
φ12	12.0	1.0±0.1	1.50±0.1	7.0	1.7±0.1	2.5±0.1	100
φ15	15.0	1.0±0.1	1.50±0.1	9.0	1.7±0.1	2.5±0.1	50
φ20	20.0	1.0±0.1	1.50±0.1	13.0	1.7±0.1	2.5±0.1	50
φ25	25.0	1.0±0.1	1.50±0.1	15.0	1.7±0.1	2.5±0.1	50
φ30	30.0	1.0±0.1	1.50±0.1	18.0	1.7±0.1	2.5±0.1	50
φ35	35.0	1.0±0.1	1.50±0.1	20.0	1.7±0.1	2.5±0.1	1
φ40	38.0	1.0±0.1	1.50±0.1	25.0	1.7±0.1	2.5±0.1	1
φ50	47.0	1.0±0.1	1.50±0.1	30.0	1.7±0.1	2.5±0.1	1
φ60	57.0	1.5±0.1	2.00±0.1	38.0	2.5±0.1	3.2±0.1	1
φ70	67.0	1.5±0.1	2.00±0.1	45.0	2.5±0.1	3.2±0.1	1
φ80	77.0	1.5±0.1	2.00±0.1	48.0	2.5±0.1	3.2±0.1	1
φ90	87.0	1.5±0.1	2.00±0.1	52.0	2.5±0.1	3.2±0.1	1
φ100	97.0	1.5±0.1	2.00±0.1	58.0	2.5±0.1	3.2±0.1	1
φ110	107.0	1.5±0.1	2.00±0.1	63.0	2.5±0.1	3.2±0.1	1

{tab=Technica Data}

Test Item	Value
Density 25℃	1.2
Rigidity JIS-A	70
Tensile strength	6.9Mpa(70Kgf/cm)
Elongation at break	400%
Tensile strength at break JIS-A	25Kgf/Cm
Volume resistance	2*12¹⁴ Ω.cm
Breakdown Voltage (1mm)	25KV
Dielectric constant (*)50Hz	3.2
Operating temperature range	-50℃-+200℃
Shrinking Ratio	about 50%
Shrinking temperature	90℃ above
RoHS Compliant	Pass (SGS report)
Low Smoking IEC 60754	Pass
Flame Retardancy UL-224	VW-1
Radiation resistance – 10⁶MGy	Pass
Chemical resistance	Not strong acid or alkali resistance
Fluid Resistance	Splash Protection of Aviation Fuel, Brake Fluid, Hydraulic Fluid, Lubricating Oil, Water
Aging 200^oC- 4hours, 180^oC-168 hours.	Pass

{/tabs}

200℃ HIGH TEMPERATURE HEAT SHRINKABLE FLUOROELASTOMER TUBING BH-200E, BH-200E(TW)

info@flypower-heatshrink.com (Super User) — Sat, 26 Apr 2014 14:18:05 +0800

HEAT SHRINKABLE FLUOROELASTOMER TUBING BH-200E, BH-200E(TW)

{tab=Specification}

Normal size		As supplied (mm)	After recovered (mm)		*Style	Standard length (m/spool)
mm	Inch	Inside diameter(Min.)	Inside diameter(Max.)	Wall thickness（Nom.）	*Style	Standard length (m/spool)
BH-200E fluoroelastomer tubing
1/8	3.2	3.2	1.6	0.76	O	50
3/16	4.8	4.8	2.4	0.90	O	50
1/4	6.4	6.4	3.2	0.90	O	50
3/8	9.5	9.5	4.8	0.90	O	50
1/2	12.7	12.7	6.4	1.10	O	30
3/4	19.1	19.1	9.5	1.30	－	30
1	25.4	25.4	12.7	1.65	－	30
1 1/2	38.1	38.1	19.1	1.90	－	15
2	50.8	50.8	25.4	2.80	－	1
BH-200E (TW) thin wall fluoroelastomer tubing
3/8	9.5	9.5	4.8	0.90	O	50
1/2	12.7	12.7	6.4	0.90	O	30
5/8	15.9	15.9	7.9	1.07	O	30
3/4	19.1	19.1	9.5	1.07	－	30
7/8	22	22	11	1.25	－	30
1	25.4	25.4	12.7	1.25	－	30
1 1/2	31.8	31.8	15.7	1.40	－	30
1 1/4	38.1	38.1	19.0	1.40	－	15
2	50.8	50.8	25.4	1.65	－	15

* O: airfilled or oval, * －: flattened

{tab=Technical Data}

Property	Test Method	Typical Data
Operating temperature	IEC 216	-55 to +200℃
Tensile strength	ASTM D 2671	≥8.5 MPa
Elongation at break	ASTM D 2671	≥250%
Elongation at break after aging	250℃, 168 hrs.	≥200%
Heat shock	300℃, 4 hrs.	No cracking
Flexibility	ASTM D 412	≤13.8MPa
Flammability	ASTM D 2671	Self-extinguish in 15sec
Volume resistance	ASTM D 876	≥109Ω.cm
Dielectric strength	ASTM D 2671	≥7.9KV/mm
Copper corrosion	SAE-AMS-DTL-23053/13(175℃/16hrs)	No corrosion

{/tabs}

150℃ DIESEL RESISTANT ELASTOMERIC HEAT SHRINKABLE TUBING BH-DR

info@flypower-heatshrink.com (Super User) — Wed, 07 May 2014 09:20:19 +0800

DIESEL RESISTANT ELASTOMERIC HEAT SHRINKABLE TUBING BH-DR,BH-DR(TW)

{tab=Specification}

Normal size		As supplied (mm)	After recovered (mm)		*Style	Standard length (m/spool)
Inch	mm	Inside diameter (Min.)	Inside diameter (Max.)	Wall thickness（Nom.）	*Style	Standard length (m/spool)
1/8	3.2	3.2	1.6	0.76	O	50
3/16	4.8	4.8	2.4	0.85	O	50
1/4	6.4	6.4	3.2	0.90	O	50
3/8	9.5	9.5	4.8	1.02	O	50
1/2	12.7	12.7	6.4	1.22	O	30
3/4	19.1	19.1	9.5	1.45	－	30
1	25.4	25.4	12.7	1.80	－	30
1- 1/2	38.1	38.1	19.1	2.40	－	15

* O: airfilled or oval, * －: flattened

{tab=Technical Data}

Property	Test Method	Typical Data
Operating temperature	IEC 216	-55 to +150oc℃
Tensile strength	ASTM D 2671	≥13 MPa
Elongation at break	ASTM D 2671	≥500%
Elongation at break after aging	160℃, 168 hrs.	≥220%
Heat shock	215℃, 4 hrs.	No cracking
Flexibility(2% secant)	ASTM D 882	≤50 MPa
Flammability	ASTM D 2671	Self-extinguish in 15sec
Volume resistance	ASTM D 876	≥109Ω.cm
Fluid resistance tensile strength	ISO37 24hrs (diesel 70℃, hydraulic 70℃,lubricant 100℃)	≥10 MPa
Fluid resistance elongation	ISO37 24hrs (diesel 70℃, hydraulic 70℃,lubricant 100℃)	≥300%

{/tabs}

260℃ PTFE TEFLON EXTRUDED TUBING BH-PTFE(N)

info@flypower-heatshrink.com (Super User) — Tue, 28 Jun 2022 10:11:53 +0800

PTFE TEFLON EXTRUDED TUBING BH-PTFE(N)

{tab=Specification}

(AWG)	Inside diameter ID(mm)	Outside DiameterOD（mm）			Package(M/Spool)
(AWG)	Inside diameter ID(mm)	S	T	L	Package(M/Spool)
30	0.30±0.10	0.80±0.10	0.70±0.10	0.60±0.10	305
28	0.38±0.10	0.88±0.10	0.78±0.10	0.68±0.10	305
26	0.46±0.10	0.96±0.10	0.86±0.10	0.76±0.10	305
24	0.56±0.10	1.16±0.10	1.06±0.10	0.86±0.10	305
23	0.66±0.10	1.26±0.10	1.16±0.10	0.96±0.10	305
22	0.71±0.10	1.31±0.10	1.21±0.10	1.01±0.10	305
21	0.81±0.10	1.41±0.10	1.31±0.10	1.11±0.10	305
20	0.86±0.10	1.66±0.10	1.46±0.10	1.16±0.10	305
19	0.96±0.20	1.76±0.20	1.56±0.20	1.26±0.20	200
18	1.07±0.20	1.87±0.20	1.67±0.20	1.37±0.20	200
17	1.19±0.20	1.99±0.20	1.79±0.20	1.49±0.20	200
16	1.34±0.20	2.14±0.20	1.94±0.20	1.64±0.20	153
15	1.50±0.20	2.30±0.20	2.10±0.20	1.80±0.20	153
14	1.68±0.20	2.48±0.20	2.28±0.20	2.00±0.20	100
13	1.93±0.20	2.73±0.20	2.53±0.20	2.25±0.20	100
12	2.16±0.25	2.96±0.25	2.76±0.25	2.50±0.25	100
11	2.41±0.25	3.21±0.25	3.01±0.25	2.76±0.25	150
10	2.69±0.25	3.49±0.25	3.29±0.25	3.04±0.25	150
9	3.00±0.25	4.00±0.25	3.80±0.25	3.40±0.25	150
8	3.38±0.25	4.38±0.25	4.18±0.25	3.78±0.25	100
7	3.76±0.25	4.76±0.25	4.56±0.25	4.16±0.25	100
6	4.22±0.25	5.22±0.25	5.02±0.25	4.72±0.25	100
5	4.72±0.25	5.72±0.25	5.52±0.25	5.20±0.25	50
4	5.28±0.30	6.28±0.30	6.08±0.30	5.88±0.25	50
3	5.94±0.30	6.94±0.30	6.74±0.30	6.54±0.25	1
2	6.68±0.30	7.68±0.30	7.48±0.30	7.28±0.25	1
1	7.46±0.30	8.46±0.30	8.26±0.30	8.06±0.25	1
0	8.38±0.30	9.38±0.30	9.18±0.30	8.98±0.25	1

{tab=Technical Data}

Property	Test Method	Typical Data
Tensile strength	ASTM D 2671	≥34.5 MPa
Elongation at break	ASTM D 2671	≥150%
Specific gravity	ASTM D 792	2.30
Heat shock	ASTM D 2671 (400℃, 4 hrs)	No cracking or dropping
Cold bend	ASTM D 2671 (-65℃, 4 hrs)	No cracking
Flammability	ASTM D 2671	Self extinguish
Volume resistance	ASTM D 2671	≥1018Ω.cm
Dielectric strength	ASTM D 2671	≥34KV/mm
Copper corrosion	UL 224	Pass
Fluid resistance	SAE-AMS-DTL-23053/12	Excellent
Water absorption	ASTM D 570	0.1 Max.

{/tabs}

260℃ PTFE TEFLON HEAT SHRINKABLE TUBING BH-PTFE

info@flypower-heatshrink.com (Super User) — Wed, 07 May 2014 08:44:24 +0800

(PTFE )TEFLON HEAT SHRINKABLE TUBING BH-PTFE

{tab=Specification}

Shrink Ratio 1.7:1

Size (mm)	As supplied ID(mm)	Fully Recovered（mm)		Package
Size (mm)	As supplied ID(mm)	ID	WT	Package
Φ1.0	1.0±0.2	≤0.6	0.20±0.05	200m/spool
Φ1.5	1.5±0.2	≤0.9	0.20±0.05	200m/spool
Φ2.0	2.0±0.2	≤1.3	0.20±0.05	200m/spool
Φ2.5	2.5±0.2	≤1.5	0.20±0.05	200m/spool
Φ3.0	3.0±0.2	≤1.8	0.20±0.05	200m/spool
Φ3.5	3.5±0.2	≤2.0	0.20±0.05	100m/spool
Φ4.0	4.0±0.3	≤2.5	0.25±0.05	100m/spool
Φ4.5	4.5±0.3	≤2.8	0.25±0.05	100m/spool
Φ5.0	5.0±0.3	≤3.0	0.25±0.05	100m/spool
Φ6.0	6.0±0.3	≤3.8	0.25±0.05	100m/spool
Φ7.0	7.0±0.3	≤4.0	0.25±0.05	100m/spool
Φ8.0	8.0±0.3	≤4.8	0.25±0.05	1m /pcs
Φ9.0	9.0±0.3	≤5.0	0.30±0.05	1m /pcs
Φ10.0	10.0±0.3	≤5.8	0.30±0.05	1m /pcs
Φ11.0	11.0±0.3	≤6.4	0.30±0.05	1m /pcs
Φ12.0	12.0±0.3	≤7.0	0.30±0.05	1m /pcs
Φ13.0	13.0±0.3	≤7.5	0.35±0.05	1m /pcs
Φ14.0	14.0±0.3	≤8.0	0.35±0.05	1m /pcs
Φ15.0	15.0±0.3	≤8.5	0.40±0.05	1m /pcs
Φ16.0	16.0±0.3	≤9.0	0.40±0.05	1m /pcs

Shrink Ratio 4:1

Size(mm)	Supplied(mm)		Fully Recovered（mm)
Size(mm)	ID	WT	ID	WT
φ2.0	2.0±0.2	0.10±0.05	≤0.50	0.30±0.05
φ2.5	2.5±0.2	0.10±0.05	≤0.65	0.30±0.05
φ3.0	3.0±0.2	0.10±0.05	≤0.80	0.30±0.05
φ3.5	3.5±0.2	0.10±0.05	≤0.90	0.30±0.05
φ4.0	4.0±0.3	0.10±0.05	≤1.0	0.30±0.05
φ4.5	4.5±0.3	0.12±0.05	≤1.15	0.30±0.05
φ5.0	5.0±0.3	0.12±0.05	≤1.25	0.30±0.05
φ6.0	6.0±0.3	0.12±0.05	≤1.5	0.30±0.05
φ7.0	7.0±0.3	0.12±0.05	≤1.75	0.30±0.05
φ8.0	8.0±0.3	0.15±0.05	≤2.0	0.35±0.05
φ9.0	9.0±0.3	0.15±0.05	≤2.25	0.35±0.05
φ10.0	10±0.3	0.15±0.05	≤2.5	0.35±0.05

{tab=Technical Data}

Property	Test Method	Typical Data
Tensile strength	ASTM D 2671	≥34.5 MPa
Elongation at break	ASTM D 2671	≥150%
Specific gravity	ASTM D 792	2.30
Heat shock	ASTM D 2671 (400℃, 4 hrs)	No cracking or dropping
Cold bend	ASTM D 2671 (-65℃, 4 hrs)	No cracking
Flammability	ASTM D 2671	Self extinguish
Volume resistance	ASTM D 2671	≥1018Ω.cm
Dielectric strength	ASTM D 2671	≥34KV/mm
Copper corrosion	UL 224	Pass
Fluid resistance	SAE-AMS-DTL-23053/12	Excellent
Water absorption	ASTM D 570	0.1 Max.

{/tabs}